Nitinol wire(TiNi memory shape wire
Name: nickel titanium wire
Application: medical, civil, chemical, etc
Specifications: Can be customized processing
Material: Nitinol
Nitinol wire (TiNi Shape Memory Alloy Wires)
1.Name: Nitinol wire (TiNi Shape Memory Alloy Wires)
2.Material: mainly Nickel and Titanium
3.Standard:ASTM F2063-05,Q/XB1516 Customer specified or Industry Standard
4.Size:Wire--0.05-6.0mm
Bar--above Dia6.0mm
Sheet--Thickness 0.3-50.0mm Width≤350mm Length≤2500mm
5.Chemical composition:Ni: 55.4% --56.2% C≤0.07 H≤0.005 O≤0.050 N:≤ 0.05
6.Aplication : Widely used in the dental arch wire, interventional stent wire, surgical sutures,
medical guide wire,eyeglass frames, mobile phone antennas and bra stand.
Quick details
| Name | Grade | Transformation Temperature AF | Form | Standard |
Shape Memory Nitinol Alloy | Ti-Ni-01 | 20 °C~ 40 °C | Wire,bar,plate | Customer specified or Industry standard |
Ti-Ni-02 | 45 °C~ 90 °C | Wire,bar,plate | ||
Superelastic Nitinol Alloy | TiNi-SS | -5 °C~ 5 °C | Wire,bar,plate | |
Low Temperature Superelastic Nitinol Alloy | TN3 | -20°C~-30°C | Wire,bar,plate | |
TNC | ||||
Medical Nitinol Alloy | TiNi-SS | 33 ± 3 °C | Wire,bar,plate | ASTM F2063 |
Narrow Hysteresis Nitinol Alloy | Ti-Ni-Cu | As-Ms ≤ 5 °C | Wire,bar | |
Wide Hysteresis Nitinol Alloy | Ti-Ni-Fe | As-Ms ≤ 150 °C | Wire, bar |
Specifications
Alloy | Chemical composition | Af (Fully annealed) | Min. elongation to failure [%] | Max. Residual elongation after 6% strain [%] | Main Applications | Specifications | |
Superelastic Ni-Ti alloy | TiNi-SS | Ti-50.8at% | -5°C ± 5°C. | 10 | 0.1 | Eyeglass Frames, Cellular Phone Antennae, Bra Underwire | Q/XB1516.2 Q/XB1516.2 |
TN3 TNC | TiNiVAl TiNiCr | -40°C ~50°C | 10 | 0.1 | |||
Body temperature Ni-Ti alloy | TiNi-YY | Ti-50.7at%Ni | Functional Af=33 ± 3 | 15 | 0.1 | Implantable devices,Bone staples Vascular Stents | ASTM 2063 |
Ti-Ni-01 | 55.6~55.8 wt%Ni | 20 - 40 | 15 | 0.1 | Guide wires, Stents Orthodontic Arches | Q/XB1516.1 | |
High temperature Ni-Ti alloy | Ti-Ni-02 | 54.8~55.5wt%Ni | 45 - 95 | 10 | 0.1 | Implantable active devices, Surgical tools, Thermostats Coffeepots | Q/XB1516 |
TiNiCu | TiNiCu | As-Ms ≤ 5 | 10 | 0.1 | |||
Density (g/cm^3) | 6.45 |
Melting point (°C ) | 1240-1310 |
Specific heat capacity( kJ/(kg·°C) | 0.46 |
Coefficient of thermal conductivity (W·m-1·K-1) |
10 |
Resistivity (10-6 Ω·m) | 80 |
Expansion coefficient (10-6 Ω·K-1 ) | 10.4 |
Elastic modulus (GPa) | 40-80 |
HV | 180-200 (low-temperature metallography) 200-350 (high-temperature metallography) |
Tensile strength (MPa) | 700-1100 |
Yield strength | 50-200 (low-temperature metallography) 100-600 (high-temperature metallography) |
Elongation δ % | 20-60 |
phase transition temperature (Af / °C) | -10-100 |
Recovery response variable % | 8, 6, 2 , <0.5 |
Utmost service temperature (°C ) | Af +60, 250 |
Maximum recovery stress (Mpa) | 680 |
Name: nickel titanium wire
Application: medical, civil, chemical, etc
Specifications: Can be customized processing
Material: Nitinol
Custom range in Φ0.05-Φ10mm, bright silk black silk, wherein Ni content is 54.5-57%, phase change temperature -15℃~100℃. The silk material has smooth surface, high dimensional precision, good plasticity, and excellent super elasticity after treatment. Medical treatment can be used for medical guide wire, dental arch wire, root canal file; Industry can be used for high-grade combination glasses frame, fishing gear, antenna, toys and other industries.