Titanium Bar AMS 4928 6AL4V
Titanium bar
Size | Dia.: 3 mm - 600 mm |
Material | Gr.1, Gr.2, Gr.4, Gr.5, Gr.7, Gr.12, Gr.23, etc. |
Standard | ASTM B348, ASTM F67, AMS 4928, ASTM F136,AMS 2631b, etc. |
Surface | Black, Pickling, Sand-blasting, Polished |
Condition | Cold rolled(Y), Hot rolled(R), Annealed (M), Quenching(C) |
Shape | Square Bar, Round Bar, Hexagonal Bar, etc. |
ZHUOHANGXIN METAL stocks a wide range of titanium bar, including a complete line of commercially pure and medical titanium bar. We can produce our products to your precise dimensions. Titanium Forged Bar, Titanium Rolled Bar, Square Titanium Bar all can be met. It can be supplied in random lengths or cut into fixed lengths.
Titanium bar is available produced and certified to Medical (ASTM F67, ASTM F136, ISO5832-2, ISO5832-3), Aerospace (AMS 4928, AMS 2631b), Industrial (ASTM B348) standards. Stock production is aligned to ASTM, AMS and ISO standards with other standards available on made to order.
Properties of titanium bar:
Titanium bar has Low Density and High Strength, Excellent Corrosion Resistance, Good resistance to effect of heat, Excellent Bearing to cryogenic property, Nonmagnetic and Non-toxic, Good thermal properties, Low Modulus of Elasticity.
Applications:
Titanium bar can be used in aircraft engines and parts, chemical equipment parts (reactors, pipes, heat exchangers and valves, etc.), ship hulls, bridges, medical implants, artificial bones, sporting products and consumer goods. Titanium bar is also used as titanium fasteners , such as titanium bolts nuts.
ZHUOHANGXIN METALcan produce titanium bar according to customers’ drawing. Special requirements will be agreed on by the titanium suppliers and titanium buyers of negotiation.ZHUOHANGXIN METALI bars for medical applications have tight tolerances and consistency in chemical composition, reducing machine set-up time and increasing cutting speeds. The excellent surface finish of ZHUOHANGXIN METAL medical bars saves polishing time and contributes to a better end-product.
Chemical requirements (Nominal %)
N | C | H | Fe | O | Al | V | Pd | Mo | Ni | Ti | |
Gr 1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | / | / | / | / | / | bal |
Gr 2 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | / | / | bal |
Gr 3 | 0.05 | 0.08 | 0.015 | 0.3 | 0.35 | / | / | / | / | / | bal |
Gr 4 | 0.05 | 0.08 | 0.015 | 0.5 | 0.4 | / | / | / | / | / | |
Gr 5 | 0.05 | 0.08 | 0.015 | 0.4 | 0.2 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
Gr 7 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
Gr 9 | 0.03 | 0.08 | 0.015 | 0.25 | 0.15 | 2.5~3.5 | 2.0~3.0 | / | / | / | bal |
Gr12 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |
Mechanical requirements
Grade | Tensil strength (min) | Yeild strength (min) | Elongation(%) | |||
ksi | MPa | ksi | MPa | |||
1 | UNSR50250 | 35 | 240 | 20 | 138 | 24 |
2 | UNSR50400 | 50 | 345 | 40 | 275 | 20 |
3 | UNSR50550 | 65 | 450 | 55 | 380 | 18 |
4 | UNSR50700 | 80 | 550 | 70 | 483 | 15 |
5 | UNSR56400 | 130 | 895 | 120 | 828 | 10 |
7 | UNSR52400 | 50 | 345 | 40 | 275 | 20 |
9 | UNSR56320 | 90 | 620 | 70 | 438 | 15 |
12 | UNSR53400 | 70 | 438 | 50 | 345 | 18 |
Testing:
Corrosion test
Eddy Current test
Mechanical test
Microstructure test
Ultrasonic test
Packaging:
With the standard plastic bags inside, wooden case or as per client’s requirement.
Production process:
Titanium Sponge---Compacting electrodes---Multiple melting---Titanium ingots---Machining---UT testing---Chemical composition inspection---Forged
billets---Forged/Rolled---Annealed----Straightening---Machining---UT testing---Visual and Dimension Inspection---UT testing---Marking---Packaging---Delivery
What is titanium best used for?
The usage of various Titanium detailed descr1ption
(1).Grade 1 can be used in the drawing parts for its good elongation and excellent corrosion-resistance.
(2).Grade 2 is used most widely in the commercially pure titanium
(3).Grade 3 is almost used in pressure,vessel.
(4).Grade 4 can be used in some fittings parts and fastening pieces, but for complex shape need 300 degree celsius to form.
(5).Alloy grade 5 widely used in the titanium alloys because of its comprehensive mechanical and chemical properties.
(6).Alloy grade 7 add little palladium in cp titanium and it has the most excellent corrosion-resistance,of course it costs higher.
(7). Alloy grade 9(Ti-3Al- 2.5V) is the most widely used in the golf clubs and bicycle girders.
(8). Alloy grade 23, ELI(extra low interstitial),can be used in the medical appliance.