Titanium Grade 2 Round Rods
Descr1ption
Titanium Grade 2 Round Rods is the most widely used CP pure titanium Rods in manufacturing today due to its good weldability, strength, ductility and formability.
Standard：ASTM B348, ASTM F136, ASTM F67,AMS4928
Diameter：Dia:Φ 6mm--Φ300mm Length: 100mm--6000mm
Delivery status：Heat treatment，Annealing treatment，Aged+Solutions
Grade 2 titanium Rods can be machined: round, flat, hexagonal, or can be customized according to your requirements.
Titanium Grade 2 Chemical composition
Grade | N | C | H | Fe | O | Al | V | Pd | Mo | Ni | Ti |
Grade 1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18 | / | / | / | / | / | Bal |
Grade 2 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | / | / | Bal |
Titanium Grade 2 Round Rods is forged by conventional processes within the narrow temperature range 815 – 900°C. Titanium and its alloys generally are more difficult to forge than both aluminium and alloy steels, due to the narrow temperature range, and high strain rate and temperature dependence of strength. Hot forging leaves a thick, extremely hard layer of titanium oxide on the surface, called “alpha case”. It is usually removed by pickling in a mixture of nitric and hydrofluoric acids. As supplied, titanium alloys are usually annealed, and can be readily cold formed in conventional machines using standard methods. When cold formed the alpha case does not form and pickling is not needed, except to remove embedded carbon steel pickup, which can cause pitting corrosion.
Titanium Billets and Bars
Titanium Grade 2 Round Rods
Grade:
GR.1, GR.2, GR.3, GR.4, GR.5 (Ti-6Al-4V), GR.7 (Ti- 0.12~0.25Pd), GR.9(Ti-3Al-2.5V) , GR.12(Ti-0.3Mo-0.8Ni), GR.23 ( Ti-6Al-4V ELI)
T35, T40, T50, T60, TA6V, 3.7024, 3.7034, 3.7055, 3.7064, 3.7164, 3.7165
Standards:
ASTM B348/ ASTM F136/ ISO 5832-3/ ASTM F67/ ISO 5832-2/ AMS 4928 and other standards.
Process:
Titanium Sponge- Compacting Electrodes- Double VAR Melting-UT testing- Peeling and Cutting- Ingots-Forging- Billets- Rolling/Precisely Forging- Annealing- Machining-UT testing- Polishing/Grinding- Inspection/Testing- Packing.
What is titanium best used for?
The usage of various Titanium detailed descr1ption
(1).Grade 1 can be used in the drawing parts for its good elongation and excellent corrosion-resistance.
(2).Grade 2 is used most widely in the commercially pure titanium
(3).Grade 3 is almost used in pressure,vessel.
(4).Grade 4 can be used in some fittings parts and fastening pieces, but for complex shape need 300 degree celsius to form.
(5).Alloy grade 5 widely used in the titanium alloys because of its comprehensive mechanical and chemical properties.
(6).Alloy grade 7 add little palladium in cp titanium and it has the most excellent corrosion-resistance,of course it costs higher.
(7). Alloy grade 9(Ti-3Al- 2.5V) is the most widely used in the golf clubs and bicycle girders.
(8). Alloy grade 23, ELI(extra low interstitial),can be used in the medical appliance.